RATE AND TEMPERATURE DEPENDENT PLASTICITY AND FAILURE OF AA7017-T73: EXPERIMENTS AND MODELLING
Año:2016
Áreas de investigación
  • Ingenieria mecanica
Datos
Descripción
A series of tensile tests on uniaxial specimens machined from different orientations with respect to the rolling direction was carried out at a wide range of loading rates for an aluminium 7017-T73 alloy. The experimental results revealed a high degree of anisotropy on both yield stress and plastic flow. In addition, the material showed very little strain-rate sensitivity. The measured fracture strains for different loading orientations showed large differences. In order to describe the material behaviour, the Yld2000-3d yield criterion and an isotropic Voce hardening model were used to describe the plasticity of the AA7017-T73. Finite element simulations showed that the plasticity model provided accurate predictions of local and global material responses under uniaxial loading. A Cockcroft-Latham failure criterion was presented for describing the anisotropic fracture behaviour of the AA7017-T73
Internacional
No
JCR del ISI
No
Título de la revista
Anales de Mecánica de la Fractura
ISSN
0213-3725
Factor de impacto JCR
Información de impacto
Volumen
33
DOI
Número de revista
Desde la página
290
Hasta la página
295
Mes
MARZO
Ranking
Esta actividad pertenece a memorias de investigación
Participantes
  • Autor: Maria Jesus Perez Martin (UPM)
  • Autor: Borja Erice (Swiss Federal Institute of Technology (ETH))
  • Autor: Francisco Rafael Galvez Diaz-Rubio (UPM)
Grupos de investigación, Departamentos, Centros e Institutos de I+D+i relacionados
  • Creador: Centro o Instituto I+D+i: CENTRO INVEST. MATERIALES ESTRUCTURALES (CIME)
  • Departamento: Ciencia de Materiales
S2i 2021 Observatorio de investigación @ UPM con la colaboración del Consejo Social UPM
Cofinanciación del MINECO en el marco del Programa INNCIDE 2011 (OTR-2011-0236)
Cofinanciación del MINECO en el marco del Programa INNPACTO (IPT-020000-2010-22)