A combined powder X-ray lattice parameter and ceramic impedance spectroscopy study is presented on materials within the CaO-CuO-TiO2 ternary phase diagram. Several compositions containing CaCu3Ti4O12 (CCTO) and small amounts of secondary phases such as TiO2, CaTiO3 and CuO are analysed and two different defect mechanisms are identified to cause non-stoichiometry in CCTO. The first mechanism involves variation in Cu content, which can explain the large differences in intrinsic bulk and extrinsic grain boundary (GB) resistance and the formation of the ceramic internal barrier layer capacitor (IBLC) structure. The second mechanism is associated with Ca-Cu anti-site disorder causing unusually high intrinsic bulk permittivity above that predicted from Clausius-Mossotti calculations.
Internacional	No
Nombre congreso	XI REUNIÓN NACIONAL DE LECTROCERÁMICA
Tipo de participación	960
Lugar del congreso	ZARAGOZA
Revisores	Si
ISBN o ISSN	0000-0000
DOI
Fecha inicio congreso	19/06/2013
Fecha fin congreso	21/06/2014
Desde la página	41
Hasta la página	41
Título de las actas	XI REUNIÓN NACIONAL DE LECTROCERÁMICA

Esta actividad pertenece a memorias de investigación

• Autor: Cintia Soledad Terny (UPM)
• Autor: Miguel Ángel De La Rubia López (UPM)
• Autor: ROBERTO E. ALONSO (UNLP-ARGENTINA)
• Autor: MARISA FLECHERO (UNLP-ARGENTINA)
• Autor: Jose de Frutos Vaquerizo (UPM)

• Creador: Grupo de Investigación: Propiedades ópticas, eléctricas y magnéticas de materiales y sus aplicaciones (POEMMA)
• Departamento: Física Aplicada a las Tecnologías de la Información