Characterisation of pre-industrial hybrid cement and effect of pre-curing temperature
Año:2016
Áreas de investigación
  • Cemento pórtland
Datos
Descripción
This study aimed to determine the physical-mechanical, mineralogical and microstructural properties of a pre-industrially manufactured hybrid cement (HYC) containing 5% alkaline activator and less than 30% clinker. The effect of the initial curing temperature (25 ± 1 or 85 °C for 20 h) on hydration kinetics and the development of compressive strength were also explored. The hydration products formed were characterised using XRD, SEM/EDX and 27Al and 29Si MAS-NMR. The findings showed that pre-industrial hybrid cement sets when hydrated with water and hardens to a 28-day mechanical strength of 35 MPa. The main reaction product formed was a mix of cementitious gels: C-(A)-S-H and C-A-S-H. Curing at 85 °C for 20 h, shows a behaviour similar to OPC, inhibited ettringite formation and generated more polymerised gels, enhancing 3-day but not 28- or 90-day mechanical strength.
Internacional
Si
JCR del ISI
Si
Título de la revista
Cement and Concrete Composites
ISSN
0958-9465
Factor de impacto JCR
4,26
Información de impacto
Volumen
73
DOI
10.1016/j.cemconcomp.2016.07.019
Número de revista
Desde la página
281
Hasta la página
288
Mes
JUNIO
Ranking
Esta actividad pertenece a memorias de investigación
Participantes
  • Autor: Bo Qu (UPM)
  • Autor: Antonia Martin Sanz (UPM)
  • Autor: Jose Ygnacio Pastor Caño (UPM)
  • Autor: Angel Palomo (Eduardo Torroja Institute for Construction Science (IETcc))
  • Autor: Ana Fernández-Jiménez (Eduardo Torroja Institute for Construction Science (IETcc))
Grupos de investigación, Departamentos, Centros e Institutos de I+D+i relacionados
  • Creador: Departamento: Ciencia de Materiales
S2i 2021 Observatorio de investigación @ UPM con la colaboración del Consejo Social UPM
Cofinanciación del MINECO en el marco del Programa INNCIDE 2011 (OTR-2011-0236)
Cofinanciación del MINECO en el marco del Programa INNPACTO (IPT-020000-2010-22)