Friction Stir Processing of AA6061-T4 Cold Rolled vs. as Cast.
Año:2008
Áreas de investigación
  • Ingenieria mecanica,
  • Materiales de construccion
Datos
Descripción
FSP of as cast AA6061: *makes an effective surface modification; FSP closed the shrinkage porosity and homogenized the as-cast microstructures by breaking up and evenly dispersing initial phases. * the material plastic deformation, flow and mechanical mixing exhibit distinctly asymmetric characteristics at advancing, retreating side zones. * the hardness increasing of as-cast AA 6061 alloy by FSP depends on the process parameters, tool rotating and advancing speed, influencing the degree of grains refinement and level of uniformity in distribution of precipitation hardening phase, Mg2Si. FSP of AA6061- T4 *The material plastic deformation, flow and mechanical mixing exhibit distinctly asymmetric characteristics at advancing, and retreating side zones *The hardness loss of AA6061-T4 alloy depends on the process parameters, tool rotating and advancing speed; the width of this soft zone depends on peak temperature and thermal cycle duration. The material softening is due to dissolution or coarsening of Mg2Si phase precipitate during FSP. *The resulted wide heat affected zone and the lower material cooling rate produced the relatively low magnitude of compressive residual stresses in the processed zone. The compressive stresses can be beneficial for reducing the crack propagation speed.
Internacional
Si
Nombre congreso
8TH INTERNATIONAL CONFERENCE ON TRENDS IN WELDING RESEARCH
Tipo de participación
960
Lugar del congreso
PINE MOUNTAIN, GEORGIA (EE.UU.)
Revisores
Si
ISBN o ISSN
0000000000
DOI
Fecha inicio congreso
01/06/2008
Fecha fin congreso
06/06/2008
Desde la página
1
Hasta la página
1
Título de las actas
TRANSPARENCIAS
Esta actividad pertenece a memorias de investigación
Participantes
  • Autor: Jaime Planas Rossello (UPM)
  • Autor: Danut Iordachescu . (UPM)
  • Autor: Mihaela Iordachescu (UPM)
  • Autor: Jesus Ruiz Hervias (UPM)
Grupos de investigación, Departamentos, Centros e Institutos de I+D+i relacionados
  • Creador: Grupo de Investigación: Ingeniería y Aplicaciones del Láser
  • Departamento: Ciencia de los Materiales
  • Centro o Instituto I+D+i: Centro Laser
  • Departamento: Física Aplicada a la Ingeniería Industrial
  • Centro o Instituto I+D+i: Centro de investigación de materiales estructurale - CIME
  • Grupo de Investigación: Materiales Estructurales Avanzados y Nanomateriales
S2i 2021 Observatorio de investigación @ UPM con la colaboración del Consejo Social UPM
Cofinanciación del MINECO en el marco del Programa INNCIDE 2011 (OTR-2011-0236)
Cofinanciación del MINECO en el marco del Programa INNPACTO (IPT-020000-2010-22)