Ti-based nanocoatings on Al2O3 powders
Año:2007
Áreas de investigación
  • Cerámicos,
  • Fisica so -- materia condensada blanda,
  • Materiales magnéticos
Datos
Descripción
Abstract: Ti-based nanocoatings on ceramic powders were successfully fabricated by heterogeneous precipitation method. Commercial Al2O3 (average particle size of 0.5 mu m), titanium tetrabutoxide (Ti(C4H9O)4) and urea (CO(NH2)(2)) have been used as starting materials. Selecting appropriate precipitation conditions, both the thickness and the uniformity of Ti-based nanocoatings were adjusted. With a molar ratio TiO2/Al2O3 = 0.05 and the use of urea in excess, a homogeneous nanocoating of similar to 20 nm on the alumina powder surface was attained. FTIR spectra indicated the formation of the TiO2-based nanocoating onto Al(2)o(3) particles and TEM examinations showed that the amorphous coating layer crystallized to < 10 nm TiO2 particles upon calcination at 500 degrees C.
Internacional
Si
JCR del ISI
Si
Título de la revista
CERAM INT
ISSN
0272-8842
Factor de impacto JCR
1,36
Información de impacto
Volumen
33
DOI
Número de revista
5
Desde la página
875
Hasta la página
878
Mes
SIN MES
Ranking
Esta actividad pertenece a memorias de investigación
Participantes
  • AUTOR: TERESA SIERRA (ICV-CSIC)
  • Autor: Marina Villegas Gracia (UPM)
  • Autor: Jose Francisco Fernández Lozano (UPM)
  • Autor: Amador Caballero Cuesta (UPM)
Grupos de investigación, Departamentos, Centros e Institutos de I+D+i relacionados
  • Creador: Grupo de Investigación: Propiedades ópticas, eléctricas y magnéticas de materiales y sus aplicaciones (POEMMA)
S2i 2021 Observatorio de investigación @ UPM con la colaboración del Consejo Social UPM
Cofinanciación del MINECO en el marco del Programa INNCIDE 2011 (OTR-2011-0236)
Cofinanciación del MINECO en el marco del Programa INNPACTO (IPT-020000-2010-22)