CORROSION FATIGUE BEHAVIOUR OF 317LN AUSTENITIC STAINLESS STEEL IN PHOSPHORIC ACID
Año:2009
Áreas de investigación
  • Materiales de construccion
Datos
Descripción
The corrosion fatigue crack-growth behaviour of AISI 317LN stainless steel was evaluated in air and in 85% phosphoric acid at 20 °C. Austenitic stainless steels with high molybdenum content have high corrosion resistance and good mechanical properties. However, this increase in the molybdenum content and other elements such as nitrogen can also modify the microstructure. This leads to a modification of its mechanical properties. The corrosion fatigue crack-growth rate was higher in phosphoric acid immersion than in air. Austenitic stainless steels with a fully austenitic microstructure were more ductile, tough, and behave better against corrosion fatigue. The higher resistance to corrosion fatigue was directly associated to its higher resistance to corrosion.
Internacional
Si
JCR del ISI
Si
Título de la revista
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING
ISSN
0308-0161
Factor de impacto JCR
0,862
Información de impacto
Volumen
86
DOI
10.1016/j.ijpvp.2009.06.001
Número de revista
10
Desde la página
656
Hasta la página
660
Mes
OCTUBRE
Ranking
Esta actividad pertenece a memorias de investigación
Participantes
  • Autor: Javier Oñoro Lopez (UPM)
Grupos de investigación, Departamentos, Centros e Institutos de I+D+i relacionados
  • Creador: Grupo de Investigación: Ingeniería y Ciencia de los Materiales
  • Centro o Instituto I+D+i: Centro Laser
  • Departamento: Ingeniería y Ciencia de los Materiales
S2i 2021 Observatorio de investigación @ UPM con la colaboración del Consejo Social UPM
Cofinanciación del MINECO en el marco del Programa INNCIDE 2011 (OTR-2011-0236)
Cofinanciación del MINECO en el marco del Programa INNPACTO (IPT-020000-2010-22)